Export Princeton University Laboratory tantalum rods
99.99% tantalum rods
Specification: Dia40*1000mm
Quantity: 5 pieces
Standard: ASTM B365
Weight: 106.2kg
Tantalum Rod (Tantalum Bar) is well-known mainly for its unmatched corrosion resistance and chemical inertness. Tantalum Rod (Tantalum Bar) is also extremely stable at high temperatures, since tantalum has a melting point around 3000°C. Tantalum is also one of the most bio-compatible metals available and is also radio-opaque due to its high density (16.68 g/cm3).
Tantalum Grades Guide:
R05200, unalloyed tantalum, electron-beam furnace or vacuum-arc melt, or both;
R05400, unalloyed tantalum, powder-metallurgy consolidation;
R05240, tantalum alloy, 60 % tantalum, 40 % niobium, electron-beam furnace or vacuum-arc melt;
R05252, tantalum alloy, 97.5 % tantalum, 2.5 % tungsten, electron-beam furnace or vacuum-arc melt, or both;
R05255, tantalum alloy, 90 % tantalum, 10 % tungsten, electron-beam furnace of vacuum-arc melt, or both.
Physical Properties:
Density 16.6 g/cc
Melting Point 3290 K, 2996°C, 5462°F
Boiling Point 5731 K, 6100°C, 9856°F
Coefficient of Thermal Expansion (20°C) 6.5 x 10(-6) / °C
Electrical Resistivity (20°C) 13.5 microhms-cm
Electrical Conductivity 13% IACS
Specific Heat 0.036 cal/g/°C
Thermal Conductivity .13 cal/cm(2)/cm°C/sec
Technology:
Tantalum Powder → Isocratic Pressing → Bar Billet →Sintering → Semi-finished bar →Forging → Swaging → Polished → End products → Inspection → Packing
Testing:
Corrosion test
Eddy Current test
Mechanical test
Microstructure test
| Grade | Condition | Diameter/mm | Length |
|
R05200 R05400 R05252 R05240 R05255 |
Cold maching(Y) Hot maching(R) Annealing(M) |
3.0~95 | ≥200 |
| FTa1FTa2 | Cold maching(Y) Annealing(M) | 3.5~5.0 | ≥500 |
| >5.0~25 | ≥300 |
| Mechanical property (Annealed) | |||
| Grade (UNS) | Tensile strength min psi (MPa) | Yield strength min psi(MPa)(2%) | Elongation min, % (1in. gage length) |
| (R05200, R05400) | 30000 (207) | 20000(138) | 20 |
| Ta-10W (RO5255) | 70000 (482) | 60000 (414) | 15 |
| Ta-2.5W (RO5252) | 40000 (276) | 30000 (207) | 20 |
| Ta-40Nb (RO5240) | 35000 (241) | 20000 (138) | 25 |
Features & Applications
Highly malleable
High specific strength
Good corrosion resistance
Superconductivity
Excellent high and low temperature properties
Rediation protection
High Melting point (2996℃)
Application
Mechanical Industry
Aerospace Industry
Car Industry
Petroleum Chemical Industry
Transportation & Construction
Electronic Industry
Shaanxi Zhuohangxin Metal Materials Co. LTD
Baoti Road, Baoji Hi-Tech Development Zone, Shaanxi Province, China
Tel: +86-13891795577
Email: sales@ti-metals.com